Flow Chart Sheet 1621 Sakazu, Kurashiki, Okayama 710-0801, Japan INDICTIONS Case -1-2 Case Case C Case D Case E Cementation of crowns, bridges, inlays and onlays Made of metal Made of conventional porcelain, ceramic, hybrid ceramics or composite resin Cementation of veneers Cementation of adhesion bridges Cementation of metal cores, resin cores, metal posts or glassfiber posts malgam bonding S501-EU-01 11/2009 1-1 S501-EU シート.indd 1 10.6.3 10:47:00 M
Dental curing unit type and light-curing time Type Light source Wavelength range and light intensity Light-curing time Conventional halogen Halogen lamp Light intensity of 300 550 mw/cm 2 in wavelength range from 400 515 nm 20 sec. Fast halogen Halogen lamp Light intensity of more than 550 mw/cm 2 in wavelength range from 400 515 nm 5 sec. Plasma arc Xenon lamp Light intensity of more than 2000 mw/cm 2 in wavelength range from 400 515 nm, and light intensity of more than 450 mw/cm 2 in wavelength range from 400 430 nm 5 sec. LED lue LED Light intensity of more than 300 mw/cm 2 in wavelength range from 400 515 nm 20 sec. We mention the abbreviated product name in this sheet. Product bbreviated product name PNVI TM F 2.0 Paste Paste PNVI TM F 2.0 ED PRIMER II ED PRIMER II LLOY PRIMER CLERFIL TM CERMIC PRIMER CERMIC PRIMER PNVI TM F 2.0 OXYGURD II OXYGURD II 1-2 S501-EU シート.indd 2 10.6.3 10:47:00 M
Case -1 Cementation of crowns, bridges, inlays and onlays made of metal 1 Sandblast, then ultrasonic 2 pply LLOY PRIMER to the 3 Mix equal amounts of ED PRIMER 4 pply mixed ED PRIMER II clean and dry. adherent surface if precious II &. Mixed ED PRIMER II to the abutment surface and metal are used. initiates set of cement. leave for 30 sec. 30 s + * The mixture must be used within 5 min. after mixing. 5 Remove any excess ED 6 Dispense equal amounts of PRIMER II and dry. paste &. 7 Mix paste & for 20 sec. 8 pply the mixture to the restoration. mark reference line 2-1 S501-EU シート.indd 3 10.6.3 10:47:06 M
Case -1 Cementation of crowns, bridges, inlays and onlays made of metal 10 -a Light-cure the margins. *Refer to the table for light-curing time 9 Cement the restoration to the abutment surface and remove the excess paste. 10 -b OR Self-cure the paste by applying OXYGURD II to the margins. Then, wait for 3 min. and wash. 3 min 2-2 S501-EU シート.indd 4 10.6.3 10:47:08 M
Case -2 Cementation of crowns, bridges, inlays and onlays made of conventional porcelain, ceramic, hybrid ceramics or composite resin 1 Sandblast, then ultrasonic 2 pply phosphoric acid (e.g. 3 pply CERMIC PRIMER clean and dry. K-ETCHNT GEL) to clean to the adherent surface, and surface for 5 sec. Rinse and dry. dry. 4 Mix equal amounts of ED PRIMER II &. Mixed ED PRIMER II initiates set of cement. 5 s ir * The mixture must be used within 5 min. after mixing. + For cementation of zircornia or alumina restorations, step 2 and 3 are not required. 5 pply mixed ED PRIMER II to the abutment surface and leave for 30 sec. 6 Remove any excess ED PRIMER II and dry. 7 Dispense equal amounts of paste &. 8 Mix paste & for 20 sec. 30 s mark reference line 3-1 S501-EU シート.indd 5 10.6.3 10:47:14 M
Case -2 Cementation of crowns, bridges, inlays and onlays made of conventional porcelain, ceramic, hybrid ceramics or composite resin 11 -a Light-cure the margins. *Refer to the table for light-curing time 9 pply the mixture to the 10 Cement the restoration to restoration. the abutment surface and remove the excess paste. 11 -b OR Self-cure the paste by applying OXYGURD II to the margins. Then, wait for 3 min. and wash. 3 min 3-2 S501-EU シート.indd 6 10.6.3 10:47:17 M
Case Cementation of veneers 1 s necessary, sandblast the 2 pply phosphoric acid (e.g. 3 pply CERMIC PRIMER 4 pply phosphoric acid (e.g. adherent surface of veneer with care K-ETCHNT GEL) to the adherent to the adherent surface, and K-ETCHNT GEL) to the enamel to prevent the edges from chipping, then ultrasonic clean and dry. surface, leave for 5 sec., wash and dry. dry. surface for 10 sec. Rinse and dry. 5 s 10 s ir ir 5 Mix equal amounts of ED PRIMER II &. Mixed ED PRIMER II initiates set of cement. 6 pply mixed ED PRIMER II to the abutment surface and leave for 30 sec. 7 Remove any excess ED PRIMER II and dry. 8 Dispense equal amounts of paste &. mark + * The mixture must be used within 5 min. after mixing. 30 s reference line 4-1 S501-EU シート.indd 7 10.6.3 10:47:22 M
Case Cementation of veneers 9 Mix paste & for 20 sec. 10 pply the mixture to the 11 Cement the veneer to the restoration. tooth and remove the excess paste. 12 -a Light-cure the margins. 12 -b Self-cure the paste by applying *Refer to the table for light-curing time. OXYGURD II to the margins. Then, wait for 3 min. and wash. OR 3 min 4-2 S501-EU シート.indd 8 10.6.3 10:47:24 M
Case C Cementation of adhesion bridges 1 Sandblast, then ultrasonic 2 pply LLOY PRIMER to the 3 pply phosphoric acid (e.g. clean and dry. adherent surface if precious K-ETCHNT GEL) to the enamel metal are used. surface for 10 sec. Rinse and dry. 4 Mix equal amounts of ED PRIMER II &. Mixed ED PRIMER II initiates set of cement. 10 s ir + C * The mixture must be used within 5 min. after mixing. 5 pply mixed ED PRIMER II to the abutment surface and leave for 30 sec. 6 Remove any excess ED PRIMER II and dry. 7 Dispense equal amounts of paste &. 8 Mix paste & for 20 sec. 30 s mark reference line 5-1 S501-EU シート.indd 9 10.6.3 10:47:29 M
Case C Cementation of adhesion bridges 11 -a Light-cure the margins. *Refer to the table for light-curing time C 9 pply the mixture to the 10 Cement the restoration to restoration. the abutment surface and remove the excess paste. 11 -b OR Self-cure the paste by applying OXYGURD II to the margins. Then, wait for 3 min. and wash. 3 min 5-2 S501-EU シート.indd 10 10.6.3 10:47:31 M
Case D Cementation of metal cores, resin cores, metal posts or glass-fiber posts 1 Treatment of post surface. 2 Mix equal amounts of ED PRIMER II &. Mixed ED PRIMER II initiates set of cement. 3 pply the mixed primer to the root canal and the cavity wall, and leave for 30 seconds. For metal post : Sandblasting, then ultrasonic clean and dry. If the post is precious metal, apply LLOY PRIMER and dry. + 30 s For glass-fiber post : pply phosphoric acid (e.g. K-ETCHNT GEL), leave for 5 sec., wash and dry. pply CERMIC PRIMER, and dry. * The mixture must be used within 5 min. after mixing. D 4 Wipe away the excess mixed primer and dry. 5 Dispense equal amounts of paste &. 6 Mix paste & for 20 sec. 7 Coat posts with mixed paste. mark reference line 6-1 S501-EU シート.indd 11 10.6.3 10:47:35 M
Case D Cementation of metal cores, resin cores, metal posts or glass-fiber posts 8 Seat posts and spread the excess paste 9 Place a build-up composite to the coronal base. Light-cure the paste. resin according to the *Refer to the table for light-curing time Instructions for use. D 6-2 S501-EU シート.indd 12 10.6.3 10:47:36 M
Case E malgam bonding 1 Mix equal amounts of ED PRIMER II &. Mixed ED PRIMER II initiates set of cement. 2 pply mixed ED PRIMER 3 Remove any excess ED II to the cavity surface and PRIMER II and dry. leave for 30 sec. 4 Dispense equal amounts of paste &. 30 s mark + * The mixture must be used within 5 min. after mixing. reference line E 5 Mix paste & for 20 sec. 6 pply mixture of paste to the cavity. 7 Mix and place the amalgam. 8 Complete the carving and remove the matrix band. 7-1 S501-EU シート.indd 13 10.6.3 10:47:40 M
Case E malgam bonding 10 -a Light-cure the margins. *Refer to the table for light-curing time. 9 Remove the excess paste. 11 Complete the polishing. E 10 -b OR Self-cure the paste by applying OXYGURD II to the margins. Then, wait for 3 min. and wash. 3 min 7-2 S501-EU シート.indd 14 10.6.3 10:47:41 M