CERASMART for PlanMill

CERASMART for PlanMill

2 introducing CERASMART for PlanMill

the first FORCE ABSORBING FLEXIBLE NANO CERAMIC CERASMART is a revolutionary block. It combines exceptional strength and unparalleled aesthetics. Best of all, it virtually will not chip, has a faster milling time, and is the easiest material to finish. With a revolutionary Flexible Nano Ceramic Matrix structure, CERASMART provides unsurpassed physical properties and impact dispersion due to the fully homogeneous and evenly distributed nano ceramic network. CERASMART is a unique dental material that combines the best characteristics of a high strength ceramic and a composite. In addition to the highest degree of flexibility, strength and breaking energy, this innovative hybrid nano ceramic helps ensure the best marginal integrity and high strength after bonding. unmatched aesthetics, milling accuracy, fastest mill time, and self polishing properties are also excellent features. Finally, this tooth-colored, naturally opalescent nano ceramic material offers properties that are almost identical to those of natural teeth, ensuring your patients the most innovative restoration on the market. As a result, CERASMART is perfectly suited for posterior, anterior, inlay, onlay, and implant restorations and also enables minimum tooth reduction for minimally-invasive restorations. The superior reliability of CERASMART, as well as its Restorations and Dentistry courtesy of Dr. Gumpei Koike. 3

FLEXIBLE NANO CERAMICS Only CERASMART consists of a flexible nano ceramic matrix with an even distribution of nano ceramic. This specially designed nano ceramic matrix makes it an ideal high strength and force absorbing restoration for all indications, especially implant supported crowns. cerasmart (Flexible Nano Ceramics) lava Ultimate (Resin Nano Ceramics) Vita Enamic (Hybrid Ceramics) first in class for Intra-oral properties Flexible, tough and fracture resistant Retains gloss over time and is self polishing Natural opalescence Physical properties of natural enamel Easy to polish High radiopacity Highly wear resistant First in class for Fabrication properties Mills quicker Virtually no chipping No need for sintering/ crystallization firing Repairable in the mouth Very gentle on milling burs 4

PHYSICAL PROPERTIES 400 THREE-POINT FLEXURAL STRENGTH (ISO 6872) 3.5 BIAXIAL FLEXURAL STRENGTH (ISO 6872) Flexural Strength Breaking Energy e.max CAD 356 Flexural Strength (MPa) 300 200 100 231 2.2 1.1 172 142 306 0.6 2.625 1.75 0.875 Breaking Energy (N cm) CERASMART LAVA Ultimate Empress CAD VITA Enamic 152 151 193 238 117 VITA Mark II 117 0.2 0.1 0 CERASMART Lava Ultimate Vita Enamic VITA Mark II e.max CAD 0 Data on file. 0 125 250 375 500 Flexural Strength (MPa) Data on file. CERASMART showed second higher strength, but the best breaking energy. That means CERASMART was a virtually fracture-proof material. The flexural strength of ceramics are often evaluated by a biaxial flexure test. According to this test, CERASMART showed higher than any other material besides e.max CAD. THERMAL DURABILITY (FLEXURAL STRENGTH) Stress VITA Enamic LAVA Ultimate BREAKING ENERGY CERASMART Flexural Strength (MPa) 240 180 120 60 Initial Value TC10000 202 141 171 163 116 100 Strain Data on file. 0 CERASMART Vita Enamic Lava Ultimate Data on file. The graph above is used to explain breaking energy. Thanks to its flexibility, CERASMART, which has a high breaking energy, is not easily broken; even under heavy pressure. Thermal durability of the blocks (5-55 o C). All of the blocks decrease in flexural strength, except CERASMART. It keeps the stength of 160 MPa/ TC1000. Lava Ultimate drops down to under 100MPa/TC1000 5

UNSURPASSED MARGINAL INTEGRITY cerasmart VITA MARK II Block e.max cad cerasmart vita enamic lava ultimate CERASMART recreated accurate designed margins without chipping. Indications 6 Inlays Onlays Crowns Veneers Implant supported crowns

Clinical images Restorations and Dentistry courtesy of Dr. Gumpei Koike. Restorations courtesy of Dr. Rich Rosenblatt. 7

Natural Opalescence CERASMART is the only material of its type to offer such natural tooth-like properties. Notice the enamel-like qualities and natural opalescence. This is only achieved with new Nano Ceramic Matrix. Photography courtesy of Joshua Polansky Traditional Composite cerasmart Traditional Composite cerasmart 8

Natural Florescence Only CERASMART has the amazing natural opalescence and florescence of natural teeth. transmitted light cerasmart lava Ultimate vita enamic e.max cad empress multi black light Natural Tooth cerasmart LAVA ultimate Vita enamic Vita Mark ll e.max cad 9

SUPERIOR GLOSS VALUE Due to the dynamic proprietary nano ceramic matrix, and its complete homogeneous nature, CERASMART is a true selfpolishing material. Not only does it stay polished longer, but it is proven to gain luster even after being roughened. This unique material is unsurpassed with its high gloss value, unique self polishing capability, and its unmatched aesthetics. Permanent Luster Polished CERASMART maintained a glossy surface never losing its shine. Roughened CERASMART showed superior gloss recovery reaching same level as polished surface with toothbrush. Self-Shining Property Roughened with #600 paper. CERASMART shows the dramatic recovery in the gloss value, whereas Lava Ultimate and VITA Enamic does not show much recovery. 100 GLOSS CHANGE WITH TOOTHBRUSH WEAR TEST (1 YEAR SIMULATION) 100 CHANGES OF GLOSS VALUE TOOTH BRUSH WEAR 75 75 Gloss (%) 50 Gloss (%) 50 25 25 0 0 0 3000 6000 9000 12000 0 3000 6000 9000 12000 Cycle Cycle CERASMART (polished) VITA Enamic (polished) LAVA Ultimate (polished) Data on file. CERASMART (roughened) VITA Enamic (roughened) LAVA Ultimate (roughened) Data on file. 10

PREPARATION DESIGN Minimum thickness of the restoration > 1. 5 mm Wall thickness...>1.5 mm Thickness at margins...>1.0 mm Pit and fissure areas...>1.5 mm Cusp areas...>1.5 mm > 1. 5 mm > 1 mm > 1.5 mm Margin preparation Deep chamfer or rounded shoulder Preparation angle Prepare tooth with about 6 taper Inlays and onlays All internal edges and angles should be rounded Avoid having margins in direct occlusal contact with the opposing tooth 11

CEMENTATION TECHNIQUE Prior to use, carefully read the instructions for use. CEMENTATION TECHNIQUE for inlays, onlays, crowns, and bridges. Sandblast with 25-50 µm alumina (0.2MPa). Without sandblasting, treat with hydrofluoric acid (5%) for 60 seconds. Clean with oil free air syringe or ultrasonic cleaner. Clean further with ethanol (alcohol). Apply silane coupling agent such as Ceramic Primer II and dry. No bonding agent is required after the application of Ceramic Primer II. For other primers, follow the manufacturer s instructions. 12 Clean and treat the tooth following the instructions of the manufacturer of the adhesive resin cement. Follow the procedure described by the manufacturer of the adhesive resin cement. Finish and polish the margins.

OPTIGLAZE color For external staining and glazing of your CERASMART restoration, use OPTIGLAZE color. OPTIGLAZE color is a nano filled glazing and staining system specially designed for CERASMART. Because of its specially formulated nano-filler technology, it is extremely wear resistant and made to last. The renowned nano-filler technology gives your restoration a high wear resistance, for long-lasting gloss with a high discoloration resistance. Indications Final glaze layer Adjustment of chroma and enamel characteristics Characterization of anterior and posterior restorations Restorations by Nikos Bellas, MDT. 13

THE GC CAD/CAM SOLUTION 3. Finishing and polishing GRADIA DIAPOLISHER 2. Scanning and milling Cerasmart Blocks 4. Characterization Optiglaze color 1. Shade Selection, HT or LT 5. Pre-Treatment Ceramic Primer II 7. Maintenance and repair Ceramic Primer II G-ænial Universal Flo 6. Cementation Using traditional resin cement techniques 14

SHADE SELECTION A3 HT A3 LT High Translucency (HT): A1 HT, A2 HT, A3 HT, A3.5 HT, B1 HT Mainly to replace enamel Use in cases of inlays, onlays, veneers, partial and full crowns Low Translucency (LT): A1 LT, A2 LT, A3 LT, A3.5 LT, B1 LT For replacement of dentin and enamel structures Use to mask discolored preparations, in particular for crowns Sizes One Bleach Shade (BL) Available in 12, 14, and 14L 15

SKUs CERASMART For PlanMill SKU PRODUCT DESCRIPTION SKU PRODUCT DESCRIPTION SKU PRODUCT DESCRIPTION 008353 CERASMART 12 PlanMill - A1 HT 5p 008375 CERASMART 14 PlanMill - A1 HT 5p 008397 CERASMART 14L PlanMill - A1 HT 5p 008354 CERASMART 12 PlanMill - A2 HT 5p 008376 CERASMART 14 PlanMill - A2 HT 5p 008398 CERASMART 14L PlanMill - A2 HT 5p 008355 CERASMART 12 PlanMill - A3 HT 5p 008377 CERASMART 14 PlanMill - A3 HT 5p 008399 CERASMART 14L PlanMill - A3 HT 5p 008356 CERASMART 12 PlanMill - A3.5 HT 5p 008378 CERASMART 14 PlanMill - A3.5 HT 5p 008400 CERASMART 14L PlanMill - A3.5 HT 5p 008357 CERASMART 12 PlanMill - B1 HT 5p 008379 CERASMART 14 PlanMill - B1 HT 5p 008401 CERASMART 14L PlanMill - B1 HT 5p 008358 CERASMART 12 PlanMill - A1 LT 5p 008380 CERASMART 14 PlanMill - A1 LT 5p 008402 CERASMART 14L PlanMill - A1 LT 5p 008359 CERASMART 12 PlanMill - A2 LT 5p 008381 CERASMART 14 PlanMill - A2 LT 5p 008403 CERASMART 14L PlanMill - A2 LT 5p 008360 CERASMART 12 PlanMill - A3 LT 5p 008382 CERASMART 14 PlanMill - A3 LT 5p 008404 CERASMART 14L PlanMill - A3 LT 5p 008361 CERASMART 12 PlanMill - A3.5 LT 5p 008383 CERASMART 14 PlanMill - A3.5 LT 5p 008405 CERASMART 14L PlanMill - A3.5 LT 5p 008362 CERASMART 12 PlanMill - B1 LT 5p 008384 CERASMART 14 PlanMill - B1 LT 5p 008406 CERASMART 14L PlanMill - B1 LT 5p 008363 CERASMART 12 PlanMill - Bleach 5p 008385 CERASMART 14 PlanMill - Bleach 5p 008407 CERASMART 14L PlanMill - Bleach 5p 16

OPTIGLAZE color SKU PRODUCT DESCRIPTION SKU PRODUCT DESCRIPTION 008408 OPTIGLAZE color Complete Set 008417 OPTIGLAZE color Red Brown 2.6mL 008409 OPTIGLAZE color A Plus 2.6mL 008418 OPTIGLAZE color Olive 2.6mL 008410 OPTIGLAZE color B Plus 2.6mL 008419 OPTIGLAZE color Grey 2.6mL 008411 OPTIGLAZE color C Plus 2.6mL 008420 OPTIGLAZE color Blue 2.6mL 008412 OPTIGLAZE color White 2.6mL 008421 OPTIGLAZE color Lavender 2.6mL 008413 OPTIGLAZE color Ivory White 2.6mL 008422 OPTIGLAZE color Pink 2.6mL 008414 OPTIGLAZE color Yellow 2.6mL 008423 OPTIGLAZE color Red 2.6mL 008415 OPTIGLAZE color Orange 2.6mL 008424 OPTIGLAZE color Clear 5mL 008416 OPTIGLAZE color Pink Orange 2.6mL 008425 OPTIGLAZE color Clear HV 5mL GRADIA DIAPOLISHER Polishing Paste SKU PRODUCT DESCRIPTION 001516 GRADIA DiaPolisher CERAMIC PRIMER II SKU PRODUCT DESCRIPTION 008551 Ceramic Primer II 3 ml 17

SKUs G-ænial Universal Flo SKU PRODUCT DESCRIPTION SKU PRODUCT DESCRIPTION 004202 G-ænial Universal Flo A1 004203 G-ænial Universal Flo A2 004204 G-ænial Universal Flo A3 004205 G-ænial Universal Flo A3.5 004206 G-ænial Universal Flo A4 004216 G-ænial Universal Flo AE (Adult Enamel) 008468 G-ænial Universal Flo AO1 004211 G-ænial Universal Flo AO2 004212 G-ænial Universal Flo AO3 004207 G-ænial Universal Flo B1 004208 G-ænial Universal Flo B2 004209 G-ænial Universal Flo B3 004213 G-ænial Universal Flo BW 004210 G-ænial Universal Flo C3 004214 G-ænial Universal Flo CV 004215 G-ænial Universal Flo JE (Junior Enamel) 004635 G-ænial Dispensing Tip II Needle Refill Contains: Quantity of 30 (Metal) dispensing tips for G-ænial Flo and G-ænial Universal Flo. 004634 G-ænial Dispensing Tip II Plastic Refill Contains: Quantity of 30 (Plastic) dispensing tips for G-ænial Flo and G-ænial Universal Flo. 18

NOTES 19

Not a registered trademark of GC America Inc. PlanMill is a registered trademark of PLANMECA. SKU #608440.02.2016.Rev1 800.323.7063 www.gcamerica.com www.gcamerica.com/training 2016 GC America Inc.