Soumen Dhara a & P. K Giri a b a Department of Physics, Indian Institute of Technology Guwahati,

Transcription

1 This article was downloaded by: [Kobe University] On: 01 April 2013, At: 20:43 Publisher: Taylor & Francis Informa Ltd Registered in England and Wales Registered Number: Registered office: Mortimer House, Mortimer Street, London W1T 3JH, UK Journal of Experimental Nanoscience Publication details, including instructions for authors and subscription information: Ti nanoparticles decorated ZnO nanowires heterostructure: photocurrent and photoluminescence properties Soumen Dhara a & P. K Giri a b a Department of Physics, Indian Institute of Technology Guwahati, Guwahati , India b Centre for Nanotechnology, Indian Institute of Technology Guwahati, Guwahati , India Version of record first published: 04 Jul To cite this article: Soumen Dhara & P. K Giri (2013): Ti nanoparticles decorated ZnO nanowires heterostructure: photocurrent and photoluminescence properties, Journal of Experimental Nanoscience, 8:3, To link to this article: PLEASE SCROLL DOWN FOR ARTICLE Full terms and conditions of use: This article may be used for research, teaching, and private study purposes. Any substantial or systematic reproduction, redistribution, reselling, loan, sub-licensing, systematic supply, or distribution in any form to anyone is expressly forbidden. The publisher does not give any warranty express or implied or make any representation that the contents will be complete or accurate or up to date. The accuracy of any instructions, formulae, and drug doses should be independently verified with primary sources. The publisher shall not be liable for any loss, actions, claims, proceedings, demand, or costs or damages whatsoever or howsoever caused arising directly or indirectly in connection with or arising out of the use of this material.

2 Journal of Experimental Nanoscience, 2013 Vol. 8, No. 3, , Ti nanoparticles decorated ZnO nanowires heterostructure: photocurrent and photoluminescence properties Soumen Dhara a and P.K. Giri ab * a Department of Physics, Indian Institute of Technology Guwahati, Guwahati , India; b Centre for Nanotechnology, Indian Institute of Technology Guwahati, Guwahati , India (Received 15 December 2011; final version received 29 March 2012) In this work, we have investigated the effect of Ti nanoparticles (NPs) decoration on the photoluminescence (PL) and photodetection behaviour of ZnO nanowires (NWs) array. ZnO/Ti NW heterostructure was fabricated by synthesising dense NW arrays by uniform decoration of Ti NPs of two different sizes on the surface of the vertically aligned ZnO NWs. The PL spectra shows systematic enhancement (four to six folds) in the UV PL intensity, and also shows corresponding changes in the visible emission with reference to the bare ZnO NWs. We found a major improvement in the photocurrent (PC) and a much faster photoresponse from the ZnO/Ti NW heterostructure. Our studies show that when the thickness of the Ti metal layer is doubled, further improvement in the PC and photoresponse time is obtained from the ZnO/Ti NW heterostructure. The enhancement in the PL and PC are explained on the basis of interfacial charge transfer between Ti NPs and ZnO NWs. Keywords: ZnO nanowires; heterostructure; photocurrent; photoluminescence 1. Introduction Due to the unique chemical and physical properties, ZnO nanowires (NWs) arrays have found innovative applications in a variety of applications ranging from field effect transistors, nanolasers to UV photodetectors [1 6]. Large surface-to-volume ratio and direct carrier conduction path in the NWs makes ZnO NWs a very important nanostructure for the use in nanoelectronic devices. As the surface-to-volume ratio in NWs is very high, the surface states play a key role on optical absorption, luminescence, photodetection and other properties. It is considered that heterostructures are superior for the modulation of selective properties of that material. Using suitable external materials for the heterostructures, one can modify the properties of the material according to its requirements [7 9]. ZnO NWs covered with dense and uniform ultra small metal nanoparticles (NPs) is one important class of heterostructures. Using suitable noble metal or low work function metal one could achieve very intense UV photoluminescence (PL) and very high photocurrent (PC) along with a significant reduction in the visible emission, which is one of the most important requirements for the application in UV LEDs or photodetectors. Lin et al. [10] and Cheng et al. [11] reported on the significant enhancement of UV PL intensity and subsequent reduction in the defect-related visible emission from the ZnO NWs covered with ultra small Au NPs. It was reported that beyond certain size of the Au NPs, the UV PL intensity starts decreasing. They proposed that the obtained *Corresponding author. giri@iitg.ernet.in 2013 Taylor & Francis

3 Journal of Experimental Nanoscience 333 enhancement is due to the defect loss along with the localised surface Plasmon assisted recombination. On the other hand, when the NWs surface is covered with Ag NPs, a significant improvement in the yellow green light emission is obtained [12]. Interestingly, it was reported that NWs covered with some metal leads to a decrease in the PL intensity [13]. Recently, we have shown that the contact formation between metal NPs and the surface of the ZnO NWs affects the PL and PC behaviours [14]. Therefore, it would be interesting to study the effect of Ti NP decoration on PL and PC properties, specially the interfacial interaction of the electrons on the photoinduced charge transport mechanism. In this work, we have fabricated the ZnO/Ti heterostructure and investigated the effect of Ti NPs decoration on the PL and photodetection properties. Ti NPs with two different sizes are decorated on the surface of the ZnO NWs. The PL spectra shows major enhancement in the UV PL intensity, whereas the PC is one order of magnitude higher than the PC of the as-grown case. The enhancement in the PL and PC is explained on the basis of interfacial charge transfer between Ti NPs and ZnO NWs. 2. Experimental details For the aqueous chemical growth of ZnO NWs, uniform distribution of ZnO nanocrystal seeds were prepared on the Si substrate by thermal decomposition of a zinc acetate precursor. First, 20 mm zinc acetate [(CH 3 COO) 2 Zn] solution in ethanol was uniformly coated on the Si substrate. Then the coated substrate was heated at 350 C for 30 min to get ZnO seed layer. The well-aligned ZnO NWs were synthesised by hydrolysis of zinc nitrate [Zn(NO 3 ) 2 ] in water in the presence of hexamethylenetetramine (HMT) on the substrate with seed layer. In this case, Zn(NO 3 ) 2 provides Zn 2þ ions required for building up ZnO NWs and HMT guide the growth direction. The above prepared substrate is dipped in to a mixture of equimolar (25 mm) concentration of zinc nitrate and HMT in DI water. The chemical reaction was carried out at 90 C for 1 hour in an autoclave. The substrate was then removed from the solution, rinsed in DI water and dried in air. The morphology and crystal structure of the as-grown ZnO NWs were characterised using field emission scanning electron microscope (FESEM, Sigma, Zeiss) and X-ray diffractometer (Seifert, 3003 T/T). For the fabrication of heterostructures, Ti NPs were deposited on the surface of the NWs by sputter deposition process for the time duration of 75 s and 150 s. The samples are named as ZnO/Ti1 and ZnO/Ti2 for the Ti deposition time of 75 s and 150 s, respectively. The formation of ZnO/Ti NW heterostructure was confirmed by high resolution transmission electron microscopy (HRTEM, JEM2100, JEOL). The approximate thickness of the Ti layers calculated from the Ti deposition rate was 5 nm and 10 nm, respectively. The exact thickness of the metal layers in each case may vary depending on the orientation of the NWs on the substrate. The sizes of the NPs are slightly larger or comparable to the approximate thickness of the Ti layer. The actual sizes of the Ti NPs are measured from HRTEM imaging. The PL spectra of all the samples were recorded with a 325 nm He Cd laser excitation using a high-resolution commercial PL spectrometer (FS 920P, Edinburgh Instruments). For comparative analysis, PL measurements on all the samples were made under identical experimental conditions. For the PC measurements, two circular Al contacts of 100 nm thickness were made on the top of the NWs by thermal evaporation process using a shadow mask. The diameter of the circular electrodes is 350 mm with a fixed separation of 2.5 mm between the electrodes. The photoresponse was measured using a picoammeter (Keithley, Model 6487) at a bias of 3 V under the illumination of monochromated UV light (wavelength 365 nm) from a 150 W xenon lamp at a light intensity of 0.5 mw/cm 2 in ON and OFF conditions. The UV light is focused

4 334 S. Dhara and P.K. Giri on the sample making sure that only the region between the two electrodes is illuminated. All the measurements were carried out at room temperature and atmospheric pressure. 3. Results and discussion Figure 1(a, b) shows the well-aligned growth of ZnO NWs on the Si substrate by aqueous chemical method with the help of ZnO seed layer. As seen from the images, high-density ZnO NWs grew vertically on the substrate over a large area and formed an array like structure. The diameters of the NWs are very small in the range nm and the length is about a few microns. During the chemical growth process, ZnO NWs preferentially nucleate from the tip near the grain boundaries between two adjacent grains in the ZnO seed film [15]. The diameter of the as-grown NWs usually depends on the grain size of the ZnO seeds. The degree of alignment in the as-grown ZnO NWs is strongly controlled by the orientation of the ZnO seed layer. Figure 1(c) shows the TEM image of the ZnO/Ti1 NWs sample after Ti NPs deposition for 75 s. It is seen that the NPs are distributed on the top as well as the side surface of the NWs. Due to the NPs decoration, the diameter of the above NW is found to be larger than that of the bare ZnO NWs. Figure 1(d) shows a magnified view of the Ti NPs decoration. The sizes of the Ti NPs vary in the range 4 6 nm. To study further about the structure of the NWs, we performed XRD measurements of the as-grown and ZnO/Ti2 NWs. The XRD result is shown in Figure 2, which shows a strong peak at corresponding to (002) planes of ZnO. The observed strong peak indicates the highly crystalline nature of the as-grown NWs with growth orientation along the c-axis of hexagonal structure of ZnO. Along with the (002) peak of ZnO crystal, the ZnO/Ti2 heterostructure shows additional peaks corresponding to the (002) and (101) lattice planes of Ti nanocrystals. Therefore, the XRD pattern of the ZnO/Ti2 Figure 1. FESEM images of the chemically grown ZnO NWs on Si substrate: (a) top view, (b) 45 tilted view, (c) TEM image of the ZnO/Ti NW heterostructure, where the Ti was deposited for 75 s, (d) a magnified side view of the above heterostructure. Both the images clearly show the decoration of the Ti NPs (marked by solid arrow) on the surface of the ZnO NWs.

5 Journal of Experimental Nanoscience 335 Figure 2. XRD patterns of the chemically grown NWs: (a) as-grown ZnO NWs and (b) ZnO/Ti2 NWs heterostructure, respectively. heterostructure confirmed that the Ti is present in a metallic phase in the heterostructure and that no other form, e.g. TiO 2, is produced during the deposition. The room temperature PL spectra of the as-grown and ZnO/Ti NW heterostructures are shown in Figure 3. The as-grown NWs exhibit near band edge (NBE) UV emission at 379 nm and a broad visible emission band in the blue green region. Gaussian multipeak fitting shows the existence of two emission bands, one at the blue region centred at 436 nm and another at the green region centred at 519 nm. The observed NBE emission is due to free excitonic recombination while the blue and green emission bands are due to the presence of interstitial zinc (Zn i ) [16] and single ionised oxygen vacancy (V þ o ) [17], respectively. The strong blue peak indicates the formation of dense interstitial zinc states in the as-grown ZnO NWs. It is known that, in the aqueous chemical method, zinc nitrate provides Zn 2þ ions whereas the H 2 O supplies the OH ions required for the oxidation of Zn 2þ ions. Due to the comparatively faster rate of hydrolysis of zinc nitrate than the H 2 O, formation of high density of interstitial zinc in the as-grown NWs is expected. After the Ti NPs decoration, the UV peak intensity is dramatically enhanced, while the intensity of blue and green emissions are relatively less enhanced. The enhancement factors of these three emissions gradually increase with the increase in Ti NPs thickness/diameter. The UV PL intensity is enhanced by a factor of 4.5 for ZnO/Ti1 heterostructure and 6.6 for ZnO/Ti2 heterostructure whereas the enhancement factors for the blue and green emissions are in the range of Therefore, the UV emission of the ZnO NWs is strongly influenced by the Ti NPs and it shows further improvement with higher thickness of Ti NPs. An earlier report shows a similar improvement in the PL intensity from the Ti doped ZnO NWs obtained by Ti plasma immersion ion implantation method [18]. It is expected that the above ZnO/Ti heterostructures will exhibit similar improvement in the PC and photoresponse behaviour. The obtained enhancement in the PL spectra from the ZnO/Ti heterostructure can be explained as follows. It is known that when a metal is brought in contact with a semiconductor,

6 336 S. Dhara and P.K. Giri Figure 3. Room temperature PL spectra of the: (a) as-grown ZnO NWs, (b) ZnO/Ti1 NWs heterostructure and (c) ZnO/Ti2 NWs heterostructure, respectively. A significant improvement in the intensity of the UV PL is obtained after the deposition of Ti NPs on the ZnO NWs. Three peaks are fitted with Gaussian line shape functions (solid line) to the experimental data (open circle). (d) Variations of enhancement factors of UV, blue and green emissions with different thickness of Ti. it induces band bending due to the equilibrium of Fermi level. Depending on the difference in the work functions of metal and semiconductor, two types of contacts may form at the metal semiconductor interface. Since the work function of ZnO (4.65 ev) [19] is larger than the Ti (4.26 ev) [20], an Ohmic contact is formed with downward band bending, which is shown schematically as an inset in Figure 4. This will facilitate the electron transfer process from Ti to the conduction band of ZnO and electron accumulation on the surface/interface will increase substantially. Therefore, even if the photon-generated electron hole pairs are separated at the interface, the radiative recombination probability of electrons on the conduction band and holes in the valence band/defect level will increase dramatically due to replenishment of electrons from Ti. As a result, both the UV and green emissions intensities increase with Ti coverage. Figure 4 shows the dark current voltage (I V) characteristics of the as-grown NWs and ZnO/Ti heterostructure. The I V characteristics show nearly linear behaviours with current in the range of na. The ZnO/Ti2 heterostructure shows a dramatic increase in the dark current as compared to the as-grown NWs. The dark current increases to 50 na from 2 na at a bias of 3 V after the decoration of the Ti NPs. The ZnO/Ti1 heterostructure also shows high dark current with a current of 18 na. As explained before, due to the downward band bending at the interface between Ti NPs and ZnO NWs, more numbers of electrons can easily transfer from Ti to the conduction band of ZnO. Under the bias, these electrons will contribute to the current conduction process resulting in a high dark current. In the ZnO/Ti2 heterostructure, due to higher thickness of Ti layer, more number of electrons can flow to the ZnO causing a systematic increase in dark current with increase in Ti coverage.

7 Journal of Experimental Nanoscience 337 Figure 4. Dark current voltage characteristics of the as-grown ZnO NWs and ZnO/Ti2 NWs heterostructure. Inset shows the energy band alignment of the above heterostructure. The solid arrow mark shows the easy transfer of electrons from the Fermi level of Ti to the conduction band of ZnO NWs, resulting in larger dark current. The photoresponse of the as-grown and ZnO/Ti heterostructures are measured under the UV light (wavelength 365 nm) pulse in ON and OFF conditions and the results are shown in Figure 5. The PC initially grows very fast, then increases slowly with time and finally saturates. Similarly, during the decay process the PC initially decreases very rapidly and then slowly reaches the dark current value. From the transient PC behaviours it is revealed that the ZnO/Ti NW heterostructures give a maximum photo-generated current, DI max (PC minus dark current) of ma for the ZnO/Ti1 heterostructure and ma for the ZnO/Ti2 heterostructure, respectively. Therefore, for the ZnO/Ti2 heterostructure DI max is one order of magnitude higher than the case of as-grown NWs (4.92 ma). The time-dependent PC growth and decay curves are fitted with the following equation, I ph ðtþ ¼ I þ A 1 ð1 e t= 1 Þ A 2 e t= 2 I ph ðtþ ¼ I ph ð1þ þ A 3 e t= 3 þ A 4 e t= 4 where I, A 1, A 2, A 3 and A 4 are positive constants and I ph ð1þ refers to the photocurrent after an infinitely long time of the decay experiment, which essentially is the dark current. The significance of each term in the PC growth and decay equations are explained in our previous work [21]. The first exponential term in the growth and decay equations corresponds to the electron-hole generation and recombination processes and the last exponential term represents the oxygen adsorption process. As expected, the photoresponse time for the as-grown NWs is very slow due to the presence of intrinsic defects/trap centres. The calculated time constants are 27.3 and s for the PC growth, 46.1 and s for PC decay, respectively. For the ZnO/ Ti heterostructure, the individual growth and decay time constants systematically reduces with the increase in Ti NPs coverage. The first component of the growth and decay time constants are reduced to 18.2 and 34.8 for the ZnO/Ti1 heterostructure and further reduced to 6.0 s and 23.3 s for the ZnO/Ti2 heterostructure, respectively. Therefore, the individual calculation of the growth and decay time constants reveals that the photoresponse rate is much improved for the ZnO/Ti NW heterostructure. Higher thickness of Ti coating shows faster photoresponse from the ZnO/Ti heterostructure. ð1þ ð2þ

8 338 S. Dhara and P.K. Giri Figure 5. Photoresponse behaviors (measured at 365 nm) of the: (a) as-grown ZnO NWs, (b) ZnO/Ti1 NWs heterostructure and (c) ZnO/Ti2 NWs heterostructure, respectively, measured at a bias voltage of 3 V. The photocurrent is measured under UV light in ON and OFF conditions. Individual growth and decay time constants are calculated from the modified bi-exponential fitting (solid line) to the experimental data points (open circle). (d) Change in time constants (1st and 2nd components of PC growth) with the thickness of Ti metal layer. To explain the faster photoresponse from the ZnO/Ti NWs heterostructure, first we need to understand the involvement of oxygen adsorption and photodesorption processes in the photoresponse of ZnO. Adsorption of oxygen molecules at the vacant sites on the surface of the ZnO NWs leads to a decrease in conductivity [22,23]. Under the UV irradiation, electron hole pairs are generated that increase the photocurrent, and oxygen molecules are released by photodesorption process. At the same time, some of the released oxygen molecules are readsorbed and it decreases the photocarriers. As a result, a steady photocurrent value is obtained after certain time. When the UV light is OFF, the electron hole pair recombination and adsorption processes dominate and the photocurrent value reaches the initial value after a certain time of decay. Therefore, the fast or slow response strongly depends on the time taken to reach the equilibrium of oxygen desorption and re-adsorption processes. In the present case, the decoration of Ti NPs induces rough surface morphology and large numbers of interface states between Ti and ZnO, which results in surface modification. We believe that, these interface traps improve the photoresponse process, resulting in comparatively faster photoresponse process. 4. Conclusion In summary, ZnO/Ti NWs heterostructure was fabricated by depositing small sizes of Ti NPs with different sizes on the surface of the chemically grown ZnO NWs and the resulting

9 Journal of Experimental Nanoscience 339 improvement in the PL and photodetection properties was investigated. The PL spectra shows a major enhancement (four to six fold) in the UV PL intensity and relatively small increment in the visible emission intensity. The PC of the ZnO/Ti NW heterostructure also shows large improvement, as compared to the case of bare ZnO NWs. The enhancement in the PL and PC are explained on the basis of interfacial charge transfer between Ti NPs and ZnO NWs. In the heterostructure case, a large number of electrons are easily transferred to the conduction band of ZnO through the interface between Ti NPs and ZnO due to the downward band bending in the ZnO. The photoresponse time is also significantly reduced for the ZnO/Ti heterostructure due to the faster relaxation of charge carriers through the rough surface induced traps. Our studies show that the higher thickness of the Ti metal results into higher improvement in the UV PL and faster photoresponse from the ZnO/Ti heterostructure. References [1] M. Sakurai, Y.G. Wang, T. Uemura, and M. Aono, Electrical properties of individual ZnO nanowires, Nanotechnology 20 (2009), Article ID [2] H.Y. Yang, S.P. Lau, S.F. Yu, and A.P. Abiyas, High temperature random lasing in ZnO nanowires, Phys. Rev. Lett. 89 (2006), Article ID [3] A. Wei, L. Pan, and W. Huang, Recent progress in the ZnO nanostructure-based sensors, Mat. Sci. Eng. B 176 (2011), pp [4] L. Vj, J. Oh, A.P. Nayak, A.M. Katzenmeyer, K.H. Gilchrist, S. Grego, N.P. Kobayashi, S.-Y. Wang, A.A. Talin, N.K. Dhar, and M.S. Islam, A perspective on nanowire photodetectors: Current status, future challenges, and opportunities, IEEE J. Sel. Top. Quantum Electron. 17 (2011), pp [5] N. Kumar, A. Dorfman, and J.-I. Hahm, Ultrasensitive DNA sequence detection using nanoscale ZnO sensor arrays, Nanotechnology 17 (2006), pp [6] A. Wei, X.W. Sun, J.X. Wang, Y. Lei, X.P. Cai, C.M. Li, Z.L. Dong, and W. Huang, Enzymatic glucose biosensor based on ZnO nanorod array grown by hydrothermal decomposition, Appl. Phys. Lett. 89 (2006), Article ID [7] A. Bera and D. Basak, Photoluminescence and photoconductivity of ZnS-coated ZnO nanowires, ACS Appl. Mater. Interfaces 2 (2009), pp [8] S. Dhara and P.K. Giri, ZnO/anthracene based nanowires heterostructure: Photoresponse and photoluminescence studies, J. Appl. Phys. 111 (2012), Article ID [9] J. Chang, C.K. Najeeb, J.-H. Lee, M. Lee, and J.-H. Kim, High-performance photoresponse from single-walled carbon nanotube zinc oxide heterojunctions, J. Phys. D: Appl. Phys. 44 (2011), Article ID [10] H.Y. Lin, C.L. Cheng, Y.Y. Chou, L.L. Huang, Y.F. Chen, and K.T. Tsen, Enhancement of band gap emission stimulated by defect loss, Opt. Express 16 (2006), pp [11] C.W. Cheng, E.J. Sie, B. Liu, C.H.A. Huan, T.C. Sum, H.D. Sun, and H.J. Fan, Surface plasmon enhanced band edge luminescence of ZnO nanorods by capping Au nanoparticles, Appl. Phys. Lett. 96 (2010), Article ID [12] C.-A. Lin, D.-S. Tsai, C.-Y. Chen, and J.-H. He, Significant enhancement of yellow green light emission of ZnO nanorod arrays using Ag island films, Nanoscale 3 (2011), pp [13] Y.J. Fang, J. Sha, Z.L. Wang, Y.T. Wan, W.W. Xia, and Y.W. Wang, Behind the change of the photoluminescence property of metal-coated ZnO nanowire arrays, Appl. Phys. Lett. 98 (2011), Article ID [14] S. Dhara and P.K. Giri, On the origin of enhanced photoconduction and photoluminescence from Au and Ti nanoparticles decorated ZnO nanowire heterostructures, J. Appl. Phys. 110 (2011), Article ID [15] C.S. Hsiao, C.H. Peng, S.Y. Chen, and S.C. Liou, Tunable growth of ZnO nanorods synthesized in aqueous solutions at low temperatures, J. Vac. Sci. Technol. B 24 (2006), pp [16] B. Lin, Z. Fu, and Y. Jia, Green luminescent center in undoped zinc oxide films deposited on silicon substrates, Appl. Phys. Lett. 79 (2001), pp [17] K. Vanheusden, W.L. Warren, C.H. Seager, D.R. Tallant, J.A. Voigt, and B.E. Gnade, Mechanisms behind green photoluminescence in ZnO phosphor powders, J. Appl. Phys. 79 (1996), pp [18] L. Liao, Z. Zhang, Y. Yang, B. Yan, H.T. Cao, L.L. Chen, G.P. Li, T. Wu, Z.X. Shen, B.K. Tay, T. Yu, and X.W. Sun, Tunable transport properties of n-type ZnO nanowires by Ti plasma immersion ion implantation, J. Appl. Phys. 104 (2008), Article ID [19] C.A. Aguilar, R. Haight, A. Mavrokefalos, B.A. Korgel, and S. Chen, Probing electronic properties of molecular engineered zinc oxide nanowires with photoelectron spectroscopy, ACS Nano 3 (2009), pp [20] D.R. Lide, CRC Handbook of Chemistry and Physics, Boca Raton, CRC, 2009.

10 340 S. Dhara and P.K. Giri [21] S. Dhara and P.K. Giri, Enhanced UV photosensitivity from rapid thermal annealed vertically aligned ZnO nanowires, Nanoscale Res. Lett. 6 (2011), Article ID 504. [22] Q.H. Li, T. Gao, Y.G. Wang, and T.H. Wang, Adsorption and desorption of oxygen probed from ZnO nanowire films by photocurrent measurements, Appl. Phys. Lett. 86 (2005), Article ID [23] C. Soci, A. Zhang, B. Xiang, S.A. Dayeh, D.P.R. Aplin, J. Park, X.Y. Bao, Y.H. Lo, and D. Wang, ZnO nanowire UV photodetectors with high internal gain, Nano Lett. 7 (2007), pp