ULTRASONIC ARRAY APPROACH FOR THE EVALUATION OF ELECTROFUSION JOINTS OF POLYETHYLENE GAS PIPING

Transcription

1 ULTRASONIC ARRAY APPROACH FOR THE EVALUATION OF ELECTROFUSION JOINTS OF POLYETHYLENE GAS PIPING H. J. Shin 1, Y. H. Jang 1, J. R. Kwan 2, H. D. Lee 3 1 INDE System Co., Ltd., Suwon, Kyunggi-do, , South Korea 2 Korea Gas Safety Corporation, Kyunggi-do, , South Korea 3 Korea Institute of Construction Technology, Kyunggi-do, , South Korea ABSTRACT. Polyethylene is a widely used material for piping. Especially the demand of polyethylene piping for gas distribution is being increased. Thousands of kilometers of polyethylene piping have joints, and the joint is the weak point that should be inspected before the pipe begins service. In this study, an ultrasonic array technique is applied for the nondestructive testing of electrofusion joints in polyethylene pipe. An ultrasonic real time imaging system and array transducers are developed for the experiments. In the process of image construction, transmission and dynamic receive focusing are used. Heating wires are individually identified in ultrasonic real time images, which means that the ultrasonic array technology provides enough resolution to tell wire signals from flaw signals. Imperfect fusion joints and soil inclusion are clearly indicated in the images. Even locations of wires are appeared as is. The ultrasonic imaging technique is a very promising method for the nondestructive testing of EF joining of PE pipe. INTRODUCTION The demand of polyethylene (PE) pipeline increased in many field. A noncorrosive characteristic of PE is great benefits for the maintenance and extended periods of service life. Therefore the integrity of PE pipeline greatly depends on the quality of joints. Especially the PE pipeline for the gas energy distribution should be carefully constructed to prevent an explosive gas from leakage, and the rate of failure should be very low. Up to date efforts to have good joints were focused on the control of the joining process to follow proper procedure. A review of the electrofusion joining process for PE piping system was performed to have PE pipe system of a high integrity [1]. And intelligent, knowledge based system for EF welding was proposed [2]. To achieve the rate of failure close to zero, nondestructive testing (NDT) is strongly recommended in addition to joining process control. However, no wellknown nondestructive testing methods exist for the PE pipe fusion joints. This paper introduces a promising NDT method for electrofusion (EF) joining of PE pipe. EF joining is one of the widespread PE pipe weld methods. An estimated annual use of EF joining (in 1993) were over 15 million, and growing [1]. Figure 1 shows a) EF joining of two PE pipes with EF coupler b) a cross section of EF coupler. Spirally wound-heating wires exist between coupler and main pipes. The distance between adjacent wires is usually few (1~3) mm. The fundamental ideas of joining

2 process are to heat the wires and to melt the inside and outside surface of coupler and main pipes, respectively, then to consolidate fusion area. In this study, ultrasonic array technique was applied to obtain the real time ultrasonic images of the cross section of electrofusion joints. In the use of ultrasonic waves to inspect the electrofusion joint, the most difficult challenge was to distinguish the wound heating wire at the joint interface from the joint failure. An ultrasonic focusing technique was used with ultrasonic phased array system and 96elements of array transducers. Zone based transmission focusing and dynamic receiving focusing was used. And electronic scanning was used to obtain real time two dimension images of the cross section of the EF joints. Different types of flaw samples were made and tested. Finally, an NDT method for the PE pipe EF joining was proposed. (a) FIGURE 1. a) EF joining of two PE pipes with EF coupler. b) Cross section of EF coupler. Nominal radius of the main pipe is 50mm and nominal thickness of coupler is about 5mm. The center-to-center distance between wires is about 2.3mm and diameter of wire is about 0.5mm ULTRASONIC ARRAY TECHNOLOGY Ultrasonic array is one of the emerging techniques to enhance NDT quality. The preliminary study on the ultrasonic array technology for the EF joint were proposed very recently [3]. A dominant benefit of the array technique over the traditional ultrasonic technique is the capability to control ultrasonic radiation beam in real time by electronics, so that the real time two-dimensional images can be obtained. Figure 2 shows the simulation results of the ultrasonic radiation beam control by electronics for (a) focusing and steering and focusing. The focusing capability increases the inspection resolution dramatically. Figure 3 shows the electronic scanning concepts of ultrasonic beam for (a) lateral scanning by consecutive activation of array elements and dynamic depth scanning by the control of aperture size. The electronic scanning of focal point and beam path provide real time imaging capability. And the zone based transmission and dynamic receive focusing increase the signal to noise ratio [4, 5]. Basically the ultrasonic array technology greatly depends on the ultrasonic array electronics, transmission and reception beam forming algorisms, and array sensors [6-9]. Because the NDT results are obtained by real time 2D images, the NDT process using array technology is a lot faster and easier to interpret the inspection results in comparison with traditional A- and B-scan UT.

3 (a) FIGURE 2. (a) Ultrasonic beam focusing and ultrasonic beam steering and focusing with array technology. (a) FIGURE 3. (a) Lateral scanning of focal points by consecutive activation of array elements and dynamic depth scanning of focal points by the control of aperture size.

4 BASIC EXPERIMENTS AND EQUIPMENT In basic experiments, ultrasonic A-scan method was used. An average velocity of the PE was measured as 2.24 Km/s, and attenuation was measured as 3.5dB/cm and 6dB/cm at 1Mhz and 3.5MHz respectively. With a non-focused 5MHz traditional normal incident single element transducer and an ultrasonic pulse receiver, PANAMETRICS 5800, it was hard to detect back wall echoes of a PE piping thicker than 2cm. Also echoes from heating wire was small and the resolution was very poor to tell flaws from heating wires, since the gap between adjacent wires were too small as shown in Figure 1. Acoustic impedance of PE pipe was measured as X10 3 pa s/m. For the NDT of the PE pipe EF joining in this study, an ultrasonic real time system and array transducers were developed. Figure 4 shows ultrasonic array transducers, each has 96 elements. The center frequency of the transducers determined as 3.5MHz, 5MHz, and 7.5MHz for the high penetration, general purpose, and high resolution respectively. Figure 5. shows a battery operated ultrasonic array system that is named AIM33. The system supports 96 array element transducers and has capability of real time 2D imaging, on screen sizing, image saving, and so on. The system could be connected with a B/W print, a PC monitor, and a head mount display. Therefore AIM33 is hand carry real field application system. (a) (c) FIGURE 4. Array transducer of 96 elements with the center frequency and dimension of (a) 3.5 MHz (120 X 80 X 40mm), 5 MHz (75 X 80 X 25mm), and (c) 7.5MHz (36 X 40 X 18mm). FIGURE 5. Battery operated ultrasonic array system, AIM33 (255 X 255 X 120mm, Approx. 4kg) developed by INDE System.

5 INSPECTION CONPTIONS FOR EF JOINTS Inspections are performed outside surface of the EF coupler as shown in Figure 5. Ultrasonic waves are focused and scanned underneath of the array transducer by ultrasonic array system. Heating wires reflects ultrasound and the wire signals are indicated in UT images. If the resolution of the ultrasonic beam is good, the heating wires are indicated individually, so that it is possible to count number of wires and to measure the distance between wires. Ultrasound is transmitted very well when the EF joint is good, in this case the fusion interface will not be detected in UT images. Imperfect fusion joints reflect ultrasound and the fusion interface will be detected in UT images. Fusion interface is forming underneath of wires, therefore the imperfect fusion interface signal will be detected underneath of wire signals in UT images. Also dislocation of wires and air or soil inclusions will be indicated in ultrasonic images. EXPERIMENTAL RESULTS Figure 6 (a) and show a good EF joint and its ultrasonic image that shows clear wire indications. All wires are individually indicated and the fusion interface is not indicated in the image, which means that the ultrasonic wave propagates very well through the interface. And the wire arrangement is well located as it should be. Figure 6 (c) and (d) show an imperfect EF joint and its ultrasonic image that shows the interface indication as well as wire indications. Because the fusion area is underneath of the wires, the imperfect interface signals are located underneath of wire indications. Figure 6 (e) and (f) show a over heated EF joint and its ultrasonic image that shows the dislocation of wire array. Figure 6 (g) and (h) show an EF joint with soil inclusion at the fusion interface and its ultrasonic image that shows the soil indication at the fusion interface area. CONCLUDING REMARKS Array technology provides good resolution and penetration power for the NDT of EF joint. In results, heating wires are individually identified in ultrasonic real time images, which means that the ultrasonic array technology provide enough resolution to tell wire signals from flaw signals. Imperfect fusion joints and soil inclusion are clearly indicated in the images. Even locations of wires are appeared as is. Therefore this array technology is a very promising method for the nondestructive testing of EF joining of PE pipe. In addition, the capability of real time displays makes the technology transfer to real field easy. ACKNOWLEDGEMENTS The author wishes to thank KOREA GAS SAFETY CORPORATION for the financial supports. The author also wishes to DAEYOUN MOLD INDUSTRIAL CO., LTD. and POLYTEC CO., LTD. for the making of various EF joining samples.

6 (a) (c) (d) (e) (f) (g) (h) FIGURE 6. The pictures of cross section of various EF joint samples are shown in (a) good joint (c) imperfect joint (e) over heated joint (g) soil inclusion joint, and the corresponding ultrasonic images are shown in (d) (f) (h) respectively.

7 REFERENCES 1. Bowman, J., A Review of the Electrofusion Joining Process for Polyethylene Pipe System, Polymer Engineering and Science, Vol. 37, No 4, pp (1997). 2. Torsun, I.S., Day, A.J., Wood, A.S., Dib, N., Rosala, G.F., Folkers, M.J., and Hinchcliff, F.A., Intelligent Knowledge Based System for Electrofusion Welding of Polyethylene Pipes, Plastic, Rubber and Composites Processing and Applications, Vol 25, No. 4, p. 191 (1996). 3. Shin, H.J., Kwan, J.-R. and Song, S.-J., Ultrasonic Real Time Imaging Technique for the Inspection of Electrofusion Joints for Polyethylene Piping, 2001 Forum for Gas Safety, edited by Korea Gas Safety Corporation, KGS , 2001 September 27, p Song, S. J., Shin, H. J., Jang, Y. H., Ultrasonic Phased Array Transducers for Nondestructive Evaluation of Steel Structures, in 26 th Review of Progress in Quantitative Nondestructive Evaluation, edited by D. O. Thompson and D. E. Chimenti, AIP Conference Proceedings 509, 1999, vol. 19A, pp Hwang, J. S., Shin, H. J., Song, S. J., Song, T. K., Digital Phased Array Ultrasonic Inspection System with Dynamic Focusing, 26 th Review of Progress in Quantitative Nondestructive Evaluation, 26 th Review of Progress in Quantitative Nondestructive Evaluation, edited by D. O. Thompson and D. E. Chimenti, AIP Conference Proceedings 509, 1999, vol. 19A, Kino, G. S.,. Acoustic waves : devices, imaging, and analog signal processing, Englewood Cliffs, NJ: Prentice-Hall, (1987). 7. Mucci, R. A., A Comparison of Efficient Beamforming Algorithms, IEEE Trans. Acoust. Speech Signal Processing, ASSP-32, , (1984). 8. Clay, A. C., Wooh, S. C., Azar, L., Wang, J., Experimental Study of Phased Array Beam Steering Characteristics, Journal of NDE, Vol. 18, No. 2, 59-71,(1999). 9. Wooh, S. C., Shi, Y., A Simulation of the Beam Steering Characteristics for Linear Phased Arrays, Journal of NDE, Vol. 18, No. 2, 39-57, (1999).

8 Keyword List Array ultrasonic, Polyethylene (PE), Electrofusion (EF) joining, Ultrasonic Image, Gas piping